Cr4+: YAG – Ngwa dị mma maka ịgbanye Q na-agafe agafe
Nkọwa ngwaahịa
Crystal Passive Q-switch na-ahọrọ maka ịdị mfe nke nrụpụta na ịrụ ọrụ, ọnụ ala dị ala, yana mbelata nha na ịdị arọ sistemu.
Cr4+: YAG kwụsiri ike na kemịkalụ, UV na-eguzogide ma ọ na-adịgide adịgide. Cr4+: YAG ga-arụ ọrụ n'ọtụtụ ọnọdụ okpomọkụ na ọnọdụ.
Igwe ọkụ dị mma nke Cr4 +: YAG dabara nke ọma maka ngwa ike dị elu.
Egosiputala nsonaazụ mara mma site na iji Cr4+: YAG dị ka ihe ntụgharị Q na-agafe agafe maka Nd: YAG lasers. A tụrụ ntụ ntụ saturation ka ọ dị ihe dịka 0.5 J/cm2. Oge mgbake ngwa ngwa nke 8.5µs, ma e jiri ya tụnyere agbaji, bara uru maka nkwụsị nke mkpọchi ọnọdụ.
Mpịakọta Q-switched obosara nke 7 ruo 70 ns yana ọnụego nkwughachi ruru 30 Hz enwetala. Nnwale ebe mmebi Laser gosipụtara AR mkpuchi Cr4+: YAG passive Q-switches karịrị 500 MW/cm2.
Ogo anya na ịdị n'otu nke Cr4+: YAG dị oke mma. Iji wedata mfu ntinye, a na-ekpuchi kristal AR. Cr4+: A na-enye kristal YAG na dayameta ọkọlọtọ yana ọtụtụ njupụta anya na ogologo iji kwekọọ na nkọwapụta gị.
Enwere ike iji ya na Nd: YAG na Nd,Ce: YAG, nha nkịtị dị ka D5*(85+5)
Uru nke Cr4+: YAG
● Nnukwu nkwụsi ike na ntụkwasị obi
● Ọ dị mfe iji rụọ ọrụ
● Ọnụ ụzọ mmebi dị elu (> 500MW / cm2)
● Dị ka ike dị elu, steeti siri ike na kọmpat na-agafe agafe Q-Switch
● Ogologo ndụ ogologo oge na ezigbo okpomọkụ conductivity
Njirimara ndị bụ isi
| Aha ngwaahịa | Cr4+: Y3Al5O12 |
| Ọdịdị kristal | Kubik |
| Ọkwa Dopant | 0.5mol-3 mol% |
| Moh ike ike | 8.5 |
| Ntụgharị ntụgharị uche | 1.82 @ 1064nm |
| Nhazi | <100>n'ime 5° ma ọ bụ n'ime 5° |
| Ọnụego nnabata nke izizi | 0.1 ~ 8.5cm @ 1064nm |
| mbufe mbufe | 3% ~ 98% |
Nka nka
| Nha | 3 ~ 20mm, H × W: 3 × 3 ~ 20 × 20mm N'elu arịrịọ nke ndị ahịa |
| Nkwenye akụkụ | Dayameta: ± 0.05mm, ogologo: ± 0.5mm |
| Emecha gbọmgbọm | Ngwunye ala 400#Gmt |
| Myirịta | ≤20" |
| Perpendicularity | ≤ 15′ |
| Ịdị nro | <λ/10 |
| Ogo elu | 20/10 (MIL-O-13830A) |
| Ogologo ogologo | 950 nm ~ 1100nm |
| mkpuchi AR Ntụleghachi | ≤ 0.2% (@1064nm) |
| Oke mmebi | ≥ 500MW/cm2 10ns 1Hz na 1064nm |
| Chamfer | <0.1 mm @ 45° |